Brand Name : LG CHEM
Model Number : LUPOX SG5200
Certification : MSDS, ROHS,REACH
Place of Origin : Korea
MOQ : 16T
Price : NEGOTIABLE ACCORDING TO ORDER QUANTITY
Payment Terms : T/T
Supply Ability : 500T PER MONTH
Delivery Time : 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT
Packaging Details : 25KG/BAG, 40BAGS PER PALLET
Place of origin : REPUBLIC of KOREA
Brand Nmae : LG CHEM
Material : PBT+PET+GF20%
Description : General Purpose
Application : IT/OA, Automotive Parts (Connector)
Module No. : LUPOX SG5200
PBT+PET+GF20% Resin LUPOX SG5200 Injection Molding Grade Engineering Plastic Material with Good Surface for Electronic and Electrical Products (Microwave Oven Door Gasket)
Quick Detail:
1. Injection Molding Grade
2. Good Surface
3. PBT+PET+GF20%
Description:
PBT+PET+GF20% Resin LUPOX SG5200 is Designed for Injection Molding. It Exhibits an Excellent Characteristic of Good Surface.
Applications:
Electronic and Electrical Products (Microwave Oven Door Gasket)
Datasheet:
Properties | Test Condition | Test Method | Unit | Typical Value |
Physical | ||||
Specific Gravity | ASTM D792 | - | 1.45 | |
Molding Shrinkage | ASTM D955 | % | 0.4 ~ 1.0 | |
Melt Flow Rate | 265℃/2.16kg | ASTM D1238 | g/10min | 29 |
Water Absorption | 23℃, 24hrs | ASTM D570 | % | 0.06 |
Mechanical | ||||
Tensile Strength, 3.2mm | ASTM D638 | |||
@ Break | 5mm/min | kg/cm2 | 1,000 | |
Tensile Elongation, 3.2mm | ASTM D638 | |||
@ Yield | 5mm/min | % | - | |
@ Break | 5mm/min | % | 4.0 | |
Flexural Strength, 3.2mm | 1.3mm/min | ASTM D790 | kg/cm2 | 1,600 |
Flexural Modulus, 3.2mm | 1.3mm/min | ASTM D790 | kg/cm2 | 62,000 |
IZOD Impact Strength, 6.4mm | ASTM D256 | |||
(Notched) | 23℃ | kg·cm/cm | 5.2 | |
Thermal | ||||
Melt Temperature | ASTM D3418 | ℃ | 223 | |
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
(Unannealed) | 18.6kg | ℃ | 200 | |
4.6kg | ℃ | 215 | ||
Flammability | UL94 | class | ||
1.5mm | class | HB | ||
Relative Temperature Index | UL 746B | |||
Electrical | ℃ | 75 | ||
Mechanical with Impact | ℃ | 75 | ||
Mechanical without Impact | ℃ | 75 | ||
Electrical | ||||
Comparative Tracking Index(CTI) | Solution A | UL 746 | PLC | - |
Volume Resistivity | 23℃ | ASTM D257 | Ohm·cm | - |
Arc Resistance | 23℃ | ASTM D495 | PLC | - |
Dielectric Strength, 1mm | 23℃ | ASTM D149 | kV/mm | - |
Processing Parameters | Unit | Value | ||
Drying Temperature | ℃ | 120 | ||
Drying Time | hrs | 4 | ~ 5 | |
Maximum Moisture Content | % | 0.02 | ||
Melt Temperature | ℃ | 255 | ~ 265 | |
Cylinder Temperature | Rear | ℃ | 245 | ~ 255 |
Middle | ℃ | 250 | ~ 260 | |
Front | ℃ | 255 | ~ 265 | |
Nozzle Temperature | ℃ | 255 | ~ 265 | |
Mold Temperature | ℃ | 80 ~ 100 | ||
Back Pressure | kg/cm2 | - | ||
Screw Speed | rpm | - |
Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2.KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
8.LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.
11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.
12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.
PBT+PET+GF20% Resin LUPOX SG5200 Injection Molding Grade Engineering Plastic Material with Good Surface for Electronic Images |